EN 1.4537 Stainless Steel vs. C99400 Brass

EN 1.4537 stainless steel belongs to the iron alloys classification, while C99400 brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.4537 stainless steel and the bottom bar is C99400 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
120
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 80
44
Tensile Strength: Ultimate (UTS), MPa 700
460 to 550
Tensile Strength: Yield (Proof), MPa 330
230 to 370

Thermal Properties

Latent Heat of Fusion, J/g 310
230
Maximum Temperature: Mechanical, °C 1100
200
Melting Completion (Liquidus), °C 1440
1070
Melting Onset (Solidus), °C 1390
1020
Specific Heat Capacity, J/kg-K 470
400
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
17
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
17

Otherwise Unclassified Properties

Base Metal Price, % relative 34
30
Density, g/cm3 8.1
8.7
Embodied Carbon, kg CO2/kg material 6.1
2.8
Embodied Energy, MJ/kg 84
45
Embodied Water, L/kg 220
310

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 270
230 to 590
Stiffness to Weight: Axial, points 14
7.5
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 24
15 to 17
Strength to Weight: Bending, points 22
15 to 17
Thermal Shock Resistance, points 15
16 to 19

Alloy Composition

Aluminum (Al), % 0
0.5 to 2.0
Carbon (C), % 0 to 0.020
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 1.0 to 2.0
83.5 to 96.5
Iron (Fe), % 36.3 to 46.1
1.0 to 3.0
Lead (Pb), % 0
0 to 0.25
Manganese (Mn), % 0 to 2.0
0 to 0.5
Molybdenum (Mo), % 4.7 to 5.7
0
Nickel (Ni), % 24 to 27
1.0 to 3.5
Nitrogen (N), % 0.17 to 0.25
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 0.7
0.5 to 2.0
Sulfur (S), % 0 to 0.010
0
Zinc (Zn), % 0
0.5 to 5.0
Residuals, % 0
0 to 0.3