EN 1.4541 Stainless Steel vs. ASTM A182 Grade F36

Both EN 1.4541 stainless steel and ASTM A182 grade F36 are iron alloys. They have 72% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4541 stainless steel and the bottom bar is ASTM A182 grade F36.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190 to 270
220
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 14 to 40
17
Fatigue Strength, MPa 190 to 330
330
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 410 to 550
440
Tensile Strength: Ultimate (UTS), MPa 600 to 900
710
Tensile Strength: Yield (Proof), MPa 220 to 570
490

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 940
410
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
39
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 16
3.4
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.2
1.7
Embodied Energy, MJ/kg 46
22
Embodied Water, L/kg 140
53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 190
110
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 830
650
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21 to 32
25
Strength to Weight: Bending, points 20 to 27
22
Thermal Diffusivity, mm2/s 4.0
10
Thermal Shock Resistance, points 14 to 20
21

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.080
0.1 to 0.17
Chromium (Cr), % 17 to 19
0 to 0.3
Copper (Cu), % 0
0.5 to 0.8
Iron (Fe), % 65.2 to 74
95 to 97.1
Manganese (Mn), % 0 to 2.0
0.8 to 1.2
Molybdenum (Mo), % 0
0.25 to 0.5
Nickel (Ni), % 9.0 to 12
1.0 to 1.3
Niobium (Nb), % 0
0.015 to 0.045
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 1.0
0.25 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.025
Titanium (Ti), % 0 to 0.7
0
Vanadium (V), % 0
0 to 0.020