EN 1.4560 Stainless Steel vs. EN 1.0558 Cast Steel

Both EN 1.4560 stainless steel and EN 1.0558 cast steel are iron alloys. They have 69% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4560 stainless steel and the bottom bar is EN 1.0558 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 50
18
Fatigue Strength, MPa 190
230
Impact Strength: V-Notched Charpy, J 91
33
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 550
640
Tensile Strength: Yield (Proof), MPa 190
340

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 940
400
Melting Completion (Liquidus), °C 1420
1470
Melting Onset (Solidus), °C 1370
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
53
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 15
1.7
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.0
1.4
Embodied Energy, MJ/kg 42
18
Embodied Water, L/kg 150
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
99
Resilience: Unit (Modulus of Resilience), kJ/m3 92
300
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
22
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 12
20

Alloy Composition

Carbon (C), % 0 to 0.035
0
Chromium (Cr), % 18 to 19
0
Copper (Cu), % 1.5 to 2.0
0
Iron (Fe), % 66.8 to 71
99.935 to 100
Manganese (Mn), % 1.5 to 2.0
0
Nickel (Ni), % 8.0 to 9.0
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0 to 0.030