EN 1.4560 Stainless Steel vs. C16200 Copper

EN 1.4560 stainless steel belongs to the iron alloys classification, while C16200 copper belongs to the copper alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4560 stainless steel and the bottom bar is C16200 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 50
2.0 to 56
Fatigue Strength, MPa 190
100 to 210
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 77
43
Shear Strength, MPa 390
190 to 390
Tensile Strength: Ultimate (UTS), MPa 550
240 to 550
Tensile Strength: Yield (Proof), MPa 190
48 to 470

Thermal Properties

Latent Heat of Fusion, J/g 290
210
Maximum Temperature: Mechanical, °C 940
370
Melting Completion (Liquidus), °C 1420
1080
Melting Onset (Solidus), °C 1370
1030
Specific Heat Capacity, J/kg-K 480
380
Thermal Conductivity, W/m-K 15
360
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
90
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
90

Otherwise Unclassified Properties

Base Metal Price, % relative 15
30
Density, g/cm3 7.8
9.0
Embodied Carbon, kg CO2/kg material 3.0
2.6
Embodied Energy, MJ/kg 42
41
Embodied Water, L/kg 150
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
10 to 99
Resilience: Unit (Modulus of Resilience), kJ/m3 92
10 to 970
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 20
7.4 to 17
Strength to Weight: Bending, points 19
9.6 to 17
Thermal Diffusivity, mm2/s 4.0
100
Thermal Shock Resistance, points 12
8.7 to 20

Alloy Composition

Cadmium (Cd), % 0
0.7 to 1.2
Carbon (C), % 0 to 0.035
0
Chromium (Cr), % 18 to 19
0
Copper (Cu), % 1.5 to 2.0
98.6 to 99.3
Iron (Fe), % 66.8 to 71
0 to 0.2
Manganese (Mn), % 1.5 to 2.0
0
Nickel (Ni), % 8.0 to 9.0
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0