EN 1.4563 Stainless Steel vs. S43932 Stainless Steel

Both EN 1.4563 stainless steel and S43932 stainless steel are iron alloys. They have 55% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4563 stainless steel and the bottom bar is S43932 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
160
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 40
25
Fatigue Strength, MPa 210
160
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
77
Shear Strength, MPa 420
300
Tensile Strength: Ultimate (UTS), MPa 620
460
Tensile Strength: Yield (Proof), MPa 250
230

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 460
570
Maximum Temperature: Mechanical, °C 1100
890
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 12
23
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 36
12
Density, g/cm3 8.1
7.7
Embodied Carbon, kg CO2/kg material 6.3
2.7
Embodied Energy, MJ/kg 87
40
Embodied Water, L/kg 240
120

Common Calculations

PREN (Pitting Resistance) 39
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
96
Resilience: Unit (Modulus of Resilience), kJ/m3 150
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 21
17
Strength to Weight: Bending, points 20
17
Thermal Diffusivity, mm2/s 3.2
6.3
Thermal Shock Resistance, points 13
16

Alloy Composition

Aluminum (Al), % 0
0 to 0.15
Carbon (C), % 0 to 0.020
0 to 0.030
Chromium (Cr), % 26 to 28
17 to 19
Copper (Cu), % 0.7 to 1.5
0
Iron (Fe), % 31.6 to 40.3
76.7 to 83
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 3.0 to 4.0
0
Nickel (Ni), % 30 to 32
0 to 0.5
Niobium (Nb), % 0
0.2 to 0.75
Nitrogen (N), % 0 to 0.1
0 to 0.030
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.7
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0
0.2 to 0.75