EN 1.4594 Stainless Steel vs. Type 2 Niobium
EN 1.4594 stainless steel belongs to the iron alloys classification, while Type 2 niobium belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is EN 1.4594 stainless steel and the bottom bar is Type 2 niobium.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
110 |
Elongation at Break, % | 11 to 17 | |
29 |
Poisson's Ratio | 0.28 | |
0.4 |
Shear Modulus, GPa | 76 | |
38 |
Tensile Strength: Ultimate (UTS), MPa | 1020 to 1170 | |
140 |
Tensile Strength: Yield (Proof), MPa | 810 to 1140 | |
82 |
Thermal Properties
Latent Heat of Fusion, J/g | 280 | |
320 |
Specific Heat Capacity, J/kg-K | 470 | |
270 |
Thermal Conductivity, W/m-K | 16 | |
52 |
Thermal Expansion, µm/m-K | 11 | |
7.3 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.9 | |
8.6 |
Embodied Water, L/kg | 130 | |
160 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 190 | |
35 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 1660 to 3320 | |
32 |
Stiffness to Weight: Axial, points | 14 | |
6.8 |
Stiffness to Weight: Bending, points | 25 | |
18 |
Strength to Weight: Axial, points | 36 to 41 | |
4.6 |
Strength to Weight: Bending, points | 29 to 31 | |
7.1 |
Thermal Diffusivity, mm2/s | 4.4 | |
23 |
Thermal Shock Resistance, points | 34 to 39 | |
13 |
Alloy Composition
Carbon (C), % | 0 to 0.070 | |
0 to 0.010 |
Chromium (Cr), % | 13 to 15 | |
0 |
Copper (Cu), % | 1.2 to 2.0 | |
0 |
Hafnium (Hf), % | 0 | |
0 to 0.020 |
Hydrogen (H), % | 0 | |
0 to 0.0015 |
Iron (Fe), % | 72.6 to 79.5 | |
0 to 0.010 |
Manganese (Mn), % | 0 to 1.0 | |
0 |
Molybdenum (Mo), % | 1.2 to 2.0 | |
0 to 0.020 |
Nickel (Ni), % | 5.0 to 6.0 | |
0 to 0.0050 |
Niobium (Nb), % | 0.15 to 0.6 | |
99.5 to 100 |
Nitrogen (N), % | 0 | |
0 to 0.010 |
Oxygen (O), % | 0 | |
0 to 0.025 |
Phosphorus (P), % | 0 to 0.040 | |
0 |
Silicon (Si), % | 0 to 0.7 | |
0 to 0.0050 |
Sulfur (S), % | 0 to 0.015 | |
0 |
Tantalum (Ta), % | 0 | |
0 to 0.3 |
Titanium (Ti), % | 0 | |
0 to 0.030 |
Tungsten (W), % | 0 | |
0 to 0.050 |
Zirconium (Zr), % | 0 | |
0 to 0.020 |