EN 1.4596 Stainless Steel vs. EN 1.4762 Stainless Steel

Both EN 1.4596 stainless steel and EN 1.4762 stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 1.4596 stainless steel and the bottom bar is EN 1.4762 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
78
Tensile Strength: Ultimate (UTS), MPa 1030 to 1600
620

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 450
440
Maximum Temperature: Mechanical, °C 790
1150
Melting Completion (Liquidus), °C 1450
1410
Melting Onset (Solidus), °C 1410
1370
Specific Heat Capacity, J/kg-K 470
490
Thermal Expansion, µm/m-K 11
10

Otherwise Unclassified Properties

Base Metal Price, % relative 15
12
Density, g/cm3 7.9
7.6
Embodied Carbon, kg CO2/kg material 3.5
2.5
Embodied Energy, MJ/kg 48
37
Embodied Water, L/kg 130
170

Common Calculations

PREN (Pitting Resistance) 19
25
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
26
Strength to Weight: Axial, points 36 to 56
23
Strength to Weight: Bending, points 29 to 39
21
Thermal Shock Resistance, points 35 to 54
22

Alloy Composition

Aluminum (Al), % 0.8 to 1.1
1.2 to 1.7
Carbon (C), % 0 to 0.015
0 to 0.12
Chromium (Cr), % 11.5 to 12.5
23 to 26
Iron (Fe), % 73.4 to 76.4
69.7 to 75.1
Manganese (Mn), % 0 to 0.1
0 to 1.0
Molybdenum (Mo), % 1.9 to 2.2
0
Nickel (Ni), % 9.2 to 10.2
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.010
0 to 0.040
Silicon (Si), % 0 to 0.1
0.7 to 1.4
Sulfur (S), % 0 to 0.0050
0 to 0.015
Titanium (Ti), % 0.28 to 0.4
0