EN 1.4596 Stainless Steel vs. C76400 Nickel Silver
EN 1.4596 stainless steel belongs to the iron alloys classification, while C76400 nickel silver belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.4596 stainless steel and the bottom bar is C76400 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 120 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 76 | |
| 46 |
| Tensile Strength: Ultimate (UTS), MPa | 1030 to 1600 | |
| 590 to 610 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 790 | |
| 190 |
| Melting Completion (Liquidus), °C | 1450 | |
| 990 |
| Melting Onset (Solidus), °C | 1410 | |
| 950 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 400 |
| Thermal Expansion, µm/m-K | 11 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 32 |
| Density, g/cm3 | 7.9 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 3.5 | |
| 4.1 |
| Embodied Energy, MJ/kg | 48 | |
| 63 |
| Embodied Water, L/kg | 130 | |
| 300 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 25 | |
| 20 |
| Strength to Weight: Axial, points | 36 to 56 | |
| 19 to 20 |
| Strength to Weight: Bending, points | 29 to 39 | |
| 18 to 19 |
| Thermal Shock Resistance, points | 35 to 54 | |
| 19 to 20 |
Alloy Composition
| Aluminum (Al), % | 0.8 to 1.1 | |
| 0 |
| Carbon (C), % | 0 to 0.015 | |
| 0 |
| Chromium (Cr), % | 11.5 to 12.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 58.5 to 61.5 |
| Iron (Fe), % | 73.4 to 76.4 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 1.9 to 2.2 | |
| 0 |
| Nickel (Ni), % | 9.2 to 10.2 | |
| 16.5 to 19.5 |
| Nitrogen (N), % | 0 to 0.020 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Sulfur (S), % | 0 to 0.0050 | |
| 0 |
| Titanium (Ti), % | 0.28 to 0.4 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 17.7 to 25 |
| Residuals, % | 0 | |
| 0 to 0.5 |