EN 1.4655 Stainless Steel vs. S15700 Stainless Steel
Both EN 1.4655 stainless steel and S15700 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is EN 1.4655 stainless steel and the bottom bar is S15700 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 23 to 25 | |
| 1.1 to 29 |
| Fatigue Strength, MPa | 320 | |
| 370 to 770 |
| Poisson's Ratio | 0.27 | |
| 0.28 |
| Shear Modulus, GPa | 78 | |
| 77 |
| Shear Strength, MPa | 460 | |
| 770 to 1070 |
| Tensile Strength: Ultimate (UTS), MPa | 720 to 730 | |
| 1180 to 1890 |
| Tensile Strength: Yield (Proof), MPa | 450 to 480 | |
| 500 to 1770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 290 |
| Maximum Temperature: Corrosion, °C | 440 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 1050 | |
| 870 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1440 |
| Melting Onset (Solidus), °C | 1370 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 15 | |
| 16 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
| 2.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 15 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 3.4 |
| Embodied Energy, MJ/kg | 41 | |
| 47 |
| Embodied Water, L/kg | 160 | |
| 140 |
Common Calculations
| PREN (Pitting Resistance) | 26 | |
| 23 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 160 | |
| 17 to 270 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 510 to 580 | |
| 640 to 4660 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 26 | |
| 42 to 67 |
| Strength to Weight: Bending, points | 23 | |
| 32 to 43 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 4.2 |
| Thermal Shock Resistance, points | 20 | |
| 39 to 63 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.75 to 1.5 |
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.090 |
| Chromium (Cr), % | 22 to 24 | |
| 14 to 16 |
| Copper (Cu), % | 1.0 to 3.0 | |
| 0 |
| Iron (Fe), % | 63.6 to 73.4 | |
| 69.6 to 76.8 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.1 to 0.6 | |
| 2.0 to 3.0 |
| Nickel (Ni), % | 3.5 to 5.5 | |
| 6.5 to 7.7 |
| Nitrogen (N), % | 0.050 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |