EN 1.4724 Stainless Steel vs. AISI 409 Stainless Steel

Both EN 1.4724 stainless steel and AISI 409 stainless steel are iron alloys. Both are furnished in the annealed condition. They have a very high 97% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4724 stainless steel and the bottom bar is AISI 409 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 16
24
Fatigue Strength, MPa 170
140
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 75
75
Shear Strength, MPa 340
270
Tensile Strength: Ultimate (UTS), MPa 550
420
Tensile Strength: Yield (Proof), MPa 280
200

Thermal Properties

Latent Heat of Fusion, J/g 290
270
Maximum Temperature: Corrosion, °C 390
450
Maximum Temperature: Mechanical, °C 850
710
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 21
25
Thermal Expansion, µm/m-K 11
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
6.5
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 2.0
2.0
Embodied Energy, MJ/kg 28
28
Embodied Water, L/kg 110
94

Common Calculations

PREN (Pitting Resistance) 13
11
Resilience: Ultimate (Unit Rupture Work), MJ/m3 73
83
Resilience: Unit (Modulus of Resilience), kJ/m3 210
100
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
15
Strength to Weight: Bending, points 19
16
Thermal Diffusivity, mm2/s 5.6
6.7
Thermal Shock Resistance, points 19
15

Alloy Composition

Aluminum (Al), % 0.7 to 1.2
0
Carbon (C), % 0 to 0.12
0 to 0.080
Chromium (Cr), % 12 to 14
10.5 to 11.7
Iron (Fe), % 82.2 to 86.6
84.9 to 89.5
Manganese (Mn), % 0 to 1.0
0 to 1.0
Nickel (Ni), % 0
0 to 0.5
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0.7 to 1.4
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0
0 to 0.75