EN 1.4724 Stainless Steel vs. SAE-AISI M47 Steel

Both EN 1.4724 stainless steel and SAE-AISI M47 steel are iron alloys. They have 86% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 1.4724 stainless steel and the bottom bar is SAE-AISI M47 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
77
Tensile Strength: Ultimate (UTS), MPa 550
810 to 2310

Thermal Properties

Latent Heat of Fusion, J/g 290
270
Melting Completion (Liquidus), °C 1430
1540
Melting Onset (Solidus), °C 1390
1500
Specific Heat Capacity, J/kg-K 490
450
Thermal Conductivity, W/m-K 21
23
Thermal Expansion, µm/m-K 11
11

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
26
Density, g/cm3 7.7
8.1
Embodied Carbon, kg CO2/kg material 2.0
7.4
Embodied Energy, MJ/kg 28
100
Embodied Water, L/kg 110
120

Common Calculations

PREN (Pitting Resistance) 13
38
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
28 to 79
Strength to Weight: Bending, points 19
24 to 48
Thermal Diffusivity, mm2/s 5.6
6.3
Thermal Shock Resistance, points 19
27 to 77

Alloy Composition

Aluminum (Al), % 0.7 to 1.2
0
Carbon (C), % 0 to 0.12
1.1 to 1.2
Chromium (Cr), % 12 to 14
3.5 to 4.0
Cobalt (Co), % 0
4.8 to 5.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 82.2 to 86.6
78.7 to 85
Manganese (Mn), % 0 to 1.0
0.15 to 0.4
Molybdenum (Mo), % 0
9.3 to 10
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0.7 to 1.4
0.2 to 0.45
Sulfur (S), % 0 to 0.015
0 to 0.030
Tungsten (W), % 0
1.3 to 1.8
Vanadium (V), % 0
1.2 to 1.4