EN 1.4935 Stainless Steel vs. EN 1.6587 Steel
Both EN 1.4935 stainless steel and EN 1.6587 steel are iron alloys. They have 88% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.4935 stainless steel and the bottom bar is EN 1.6587 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 880 | |
| 520 to 1420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 740 | |
| 440 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 24 | |
| 41 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 8.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.0 | |
| 3.8 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 1.7 |
| Embodied Energy, MJ/kg | 42 | |
| 22 |
| Embodied Water, L/kg | 100 | |
| 58 |
Common Calculations
| PREN (Pitting Resistance) | 16 | |
| 2.6 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 28 to 31 | |
| 18 to 50 |
| Strength to Weight: Bending, points | 24 to 26 | |
| 18 to 36 |
| Thermal Diffusivity, mm2/s | 6.5 | |
| 11 |
| Thermal Shock Resistance, points | 27 to 30 | |
| 15 to 42 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0.17 to 0.24 | |
| 0.15 to 0.21 |
| Chromium (Cr), % | 11 to 12.5 | |
| 1.5 to 1.8 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 83 to 86.7 | |
| 94.4 to 96.4 |
| Manganese (Mn), % | 0.3 to 0.8 | |
| 0.5 to 0.9 |
| Molybdenum (Mo), % | 0.8 to 1.2 | |
| 0.25 to 0.35 |
| Nickel (Ni), % | 0.3 to 0.8 | |
| 1.4 to 1.7 |
| Oxygen (O), % | 0 | |
| 0 to 0.0020 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.1 to 0.5 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Tungsten (W), % | 0.4 to 0.6 | |
| 0 |
| Vanadium (V), % | 0.2 to 0.35 | |
| 0 |