EN 1.4935 Stainless Steel vs. SAE-AISI 4130 Steel
Both EN 1.4935 stainless steel and SAE-AISI 4130 steel are iron alloys. They have 87% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.4935 stainless steel and the bottom bar is SAE-AISI 4130 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 16 to 18 | |
| 13 to 26 |
| Fatigue Strength, MPa | 350 to 400 | |
| 320 to 660 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 73 |
| Shear Strength, MPa | 480 to 540 | |
| 340 to 640 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 880 | |
| 530 to 1040 |
| Tensile Strength: Yield (Proof), MPa | 570 to 670 | |
| 440 to 980 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 740 | |
| 420 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 24 | |
| 43 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.0 | |
| 2.4 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 1.5 |
| Embodied Energy, MJ/kg | 42 | |
| 20 |
| Embodied Water, L/kg | 100 | |
| 50 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 | |
| 83 to 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 830 to 1160 | |
| 500 to 2550 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 28 to 31 | |
| 19 to 37 |
| Strength to Weight: Bending, points | 24 to 26 | |
| 19 to 29 |
| Thermal Diffusivity, mm2/s | 6.5 | |
| 12 |
| Thermal Shock Resistance, points | 27 to 30 | |
| 16 to 31 |
Alloy Composition
| Carbon (C), % | 0.17 to 0.24 | |
| 0.28 to 0.33 |
| Chromium (Cr), % | 11 to 12.5 | |
| 0.8 to 1.1 |
| Iron (Fe), % | 83 to 86.7 | |
| 97.3 to 98.2 |
| Manganese (Mn), % | 0.3 to 0.8 | |
| 0.4 to 0.6 |
| Molybdenum (Mo), % | 0.8 to 1.2 | |
| 0.15 to 0.25 |
| Nickel (Ni), % | 0.3 to 0.8 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.035 |
| Silicon (Si), % | 0.1 to 0.5 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.040 |
| Tungsten (W), % | 0.4 to 0.6 | |
| 0 |
| Vanadium (V), % | 0.2 to 0.35 | |
| 0 |