EN 1.4982 Stainless Steel vs. Solder Alloy 111

EN 1.4982 stainless steel belongs to the iron alloys classification, while solder alloy 111 belongs to the otherwise unclassified metals. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.4982 stainless steel and the bottom bar is solder alloy 111.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 230
14
Elastic (Young's, Tensile) Modulus, GPa 200
33
Elongation at Break, % 28
35
Poisson's Ratio 0.28
0.4
Shear Modulus, GPa 76
12
Tensile Strength: Ultimate (UTS), MPa 750
41

Thermal Properties

Latent Heat of Fusion, J/g 290
41
Melting Completion (Liquidus), °C 1430
220
Melting Onset (Solidus), °C 1390
180
Specific Heat Capacity, J/kg-K 470
180
Thermal Conductivity, W/m-K 13
48
Thermal Expansion, µm/m-K 16
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
11
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
11

Otherwise Unclassified Properties

Density, g/cm3 7.8
9.3
Embodied Carbon, kg CO2/kg material 4.9
9.4
Embodied Energy, MJ/kg 71
160
Embodied Water, L/kg 150
830

Common Calculations

Stiffness to Weight: Axial, points 14
2.0
Stiffness to Weight: Bending, points 25
12
Strength to Weight: Axial, points 27
1.2
Strength to Weight: Bending, points 23
2.8
Thermal Diffusivity, mm2/s 3.4
29
Thermal Shock Resistance, points 17
3.5

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Boron (B), % 0.0030 to 0.0090
0
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0.070 to 0.13
0
Chromium (Cr), % 14 to 16
0
Copper (Cu), % 0
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 61.8 to 69.7
0 to 0.020
Lead (Pb), % 0
48.8 to 50.5
Manganese (Mn), % 5.5 to 7.0
0
Molybdenum (Mo), % 0.8 to 1.2
0
Nickel (Ni), % 9.0 to 11
0 to 0.010
Niobium (Nb), % 0.75 to 1.3
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
49.5 to 50.5
Vanadium (V), % 0.15 to 0.4
0
Zinc (Zn), % 0
0 to 0.0010