EN 1.7241 Steel vs. EN 1.4563 Stainless Steel

Both EN 1.7241 steel and EN 1.4563 stainless steel are iron alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.7241 steel and the bottom bar is EN 1.4563 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 480
200
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 660 to 1990
620

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 420
1100
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
12
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
36
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.5
6.3
Embodied Energy, MJ/kg 20
87
Embodied Water, L/kg 51
240

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23 to 71
21
Strength to Weight: Bending, points 21 to 45
20
Thermal Diffusivity, mm2/s 12
3.2
Thermal Shock Resistance, points 19 to 59
13

Alloy Composition

Carbon (C), % 0.56 to 0.64
0 to 0.020
Chromium (Cr), % 0.7 to 1.0
26 to 28
Copper (Cu), % 0
0.7 to 1.5
Iron (Fe), % 96.6 to 97.8
31.6 to 40.3
Manganese (Mn), % 0.7 to 1.0
0 to 2.0
Molybdenum (Mo), % 0.25 to 0.35
3.0 to 4.0
Nickel (Ni), % 0
30 to 32
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.4
0 to 0.7
Sulfur (S), % 0 to 0.025
0 to 0.010