EN 1.7323 Steel vs. AWS E383

Both EN 1.7323 steel and AWS E383 are iron alloys. They have a modest 36% of their average alloy composition in common, which, by itself, doesn't mean much. There are 21 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.7323 steel and the bottom bar is AWS E383.

EN 1.7323 (20MoCrS4) Chromium-Molybdenum Steel AWS E383 (W88028) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		210

Poisson's Ratio		0.29
Poisson's Ratio		0.28

Shear Modulus, GPa		73
Shear Modulus, GPa		80

Tensile Strength: Ultimate (UTS), MPa		480 to 1460
Tensile Strength: Ultimate (UTS), MPa		580

Thermal Properties

Latent Heat of Fusion, J/g		250
Latent Heat of Fusion, J/g		320

Melting Completion (Liquidus), °C		1460
Melting Completion (Liquidus), °C		1420

Melting Onset (Solidus), °C		1420
Melting Onset (Solidus), °C		1370

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		470

Thermal Conductivity, W/m-K		45
Thermal Conductivity, W/m-K		12

Thermal Expansion, µm/m-K		13
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Base Metal Price, % relative		2.5
Base Metal Price, % relative		37

Density, g/cm³		7.9
Density, g/cm³		8.1

Embodied Carbon, kg CO₂/kg material		1.5
Embodied Carbon, kg CO₂/kg material		6.4

Embodied Energy, MJ/kg		20
Embodied Energy, MJ/kg		89

Embodied Water, L/kg		50
Embodied Water, L/kg		240

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		17 to 52
Strength to Weight: Axial, points		20

Strength to Weight: Bending, points		17 to 36
Strength to Weight: Bending, points		19

Thermal Diffusivity, mm²/s		12
Thermal Diffusivity, mm²/s		3.1

Thermal Shock Resistance, points		14 to 43
Thermal Shock Resistance, points		15

Alloy Composition

Carbon (C), %		0.17 to 0.23
Carbon (C), %		0 to 0.030

Chromium (Cr), %		0.3 to 0.6
Chromium (Cr), %		26.5 to 29

Copper (Cu), %		0 to 0.25
Copper (Cu), %		0.6 to 1.5

Iron (Fe), %		97.1 to 98.4
Iron (Fe), %		28.8 to 39.2

Manganese (Mn), %		0.7 to 1.0
Manganese (Mn), %		0.5 to 2.5

Molybdenum (Mo), %		0.4 to 0.5
Molybdenum (Mo), %		3.2 to 4.2

Nickel (Ni), %		0
Nickel (Ni), %		30 to 33

Phosphorus (P), %		0 to 0.025
Phosphorus (P), %		0 to 0.020

Silicon (Si), %		0 to 0.3
Silicon (Si), %		0 to 0.9

Sulfur (S), %		0.020 to 0.040
Sulfur (S), %		0 to 0.020