EN 1.7335 Steel vs. ACI-ASTM CK3MCuN Steel

Both EN 1.7335 steel and ACI-ASTM CK3MCuN steel are iron alloys. They have 55% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.7335 steel and the bottom bar is ACI-ASTM CK3MCuN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 160
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 21 to 22
39
Fatigue Strength, MPa 200 to 220
250
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 500 to 520
620
Tensile Strength: Yield (Proof), MPa 280 to 310
290

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 430
1090
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1420
1350
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 44
12
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
29
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 1.6
5.6
Embodied Energy, MJ/kg 21
76
Embodied Water, L/kg 52
190

Common Calculations

PREN (Pitting Resistance) 2.7
45
Resilience: Ultimate (Unit Rupture Work), MJ/m3 91 to 97
200
Resilience: Unit (Modulus of Resilience), kJ/m3 210 to 260
210
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
21
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 12
3.2
Thermal Shock Resistance, points 15
14

Alloy Composition

Carbon (C), % 0.080 to 0.18
0 to 0.025
Chromium (Cr), % 0.7 to 1.2
19.5 to 20.5
Copper (Cu), % 0 to 0.3
0.5 to 1.0
Iron (Fe), % 96.4 to 98.4
49.5 to 56.3
Manganese (Mn), % 0.4 to 1.0
0 to 1.2
Molybdenum (Mo), % 0.4 to 0.6
6.0 to 7.0
Nickel (Ni), % 0
17.5 to 19.5
Nitrogen (N), % 0 to 0.012
0.18 to 0.24
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.010