EN 1.7366 Steel vs. AWS E383

Both EN 1.7366 steel and AWS E383 are iron alloys. They have 40% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.7366 steel and the bottom bar is AWS E383.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 17 to 19
34
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
80
Tensile Strength: Ultimate (UTS), MPa 460 to 710
580

Thermal Properties

Latent Heat of Fusion, J/g 260
320
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
12
Thermal Expansion, µm/m-K 13
14

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
37
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.7
6.4
Embodied Energy, MJ/kg 23
89
Embodied Water, L/kg 69
240

Common Calculations

PREN (Pitting Resistance) 6.8
40
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 16 to 25
20
Strength to Weight: Bending, points 17 to 23
19
Thermal Diffusivity, mm2/s 11
3.1
Thermal Shock Resistance, points 13 to 20
15

Alloy Composition

Carbon (C), % 0 to 0.18
0 to 0.030
Chromium (Cr), % 4.0 to 6.0
26.5 to 29
Copper (Cu), % 0
0.6 to 1.5
Iron (Fe), % 91.9 to 95.3
28.8 to 39.2
Manganese (Mn), % 0.3 to 0.8
0.5 to 2.5
Molybdenum (Mo), % 0.45 to 0.65
3.2 to 4.2
Nickel (Ni), % 0
30 to 33
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.4
0 to 0.9
Sulfur (S), % 0 to 0.015
0 to 0.020