EN 1.7367 Steel vs. EN 1.0107 Steel
Both EN 1.7367 steel and EN 1.0107 steel are iron alloys. They have 90% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.7367 steel and the bottom bar is EN 1.0107 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 200 | |
110 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 18 | |
29 |
Fatigue Strength, MPa | 310 | |
160 |
Impact Strength: V-Notched Charpy, J | 31 | |
38 |
Poisson's Ratio | 0.28 | |
0.29 |
Shear Modulus, GPa | 75 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 670 | |
380 |
Tensile Strength: Yield (Proof), MPa | 460 | |
210 |
Thermal Properties
Latent Heat of Fusion, J/g | 270 | |
250 |
Maximum Temperature: Mechanical, °C | 600 | |
400 |
Melting Completion (Liquidus), °C | 1460 | |
1460 |
Melting Onset (Solidus), °C | 1420 | |
1420 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Conductivity, W/m-K | 26 | |
51 |
Thermal Expansion, µm/m-K | 13 | |
12 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 8.9 | |
7.1 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
8.2 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 7.0 | |
2.1 |
Density, g/cm3 | 7.8 | |
7.9 |
Embodied Carbon, kg CO2/kg material | 2.6 | |
1.5 |
Embodied Energy, MJ/kg | 37 | |
19 |
Embodied Water, L/kg | 88 | |
47 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
95 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 560 | |
110 |
Stiffness to Weight: Axial, points | 14 | |
13 |
Stiffness to Weight: Bending, points | 25 | |
24 |
Strength to Weight: Axial, points | 24 | |
13 |
Strength to Weight: Bending, points | 22 | |
15 |
Thermal Diffusivity, mm2/s | 6.9 | |
14 |
Thermal Shock Resistance, points | 19 | |
12 |
Alloy Composition
Aluminum (Al), % | 0 to 0.020 | |
0 |
Carbon (C), % | 0.080 to 0.12 | |
0 to 0.13 |
Chromium (Cr), % | 8.0 to 9.5 | |
0 to 0.3 |
Copper (Cu), % | 0 | |
0 to 0.3 |
Iron (Fe), % | 87.3 to 90.3 | |
97.7 to 100 |
Manganese (Mn), % | 0.3 to 0.6 | |
0 to 0.7 |
Molybdenum (Mo), % | 0.85 to 1.1 | |
0 to 0.080 |
Nickel (Ni), % | 0 to 0.4 | |
0 to 0.3 |
Niobium (Nb), % | 0.060 to 0.1 | |
0 to 0.010 |
Nitrogen (N), % | 0.030 to 0.070 | |
0 |
Phosphorus (P), % | 0 to 0.030 | |
0 to 0.025 |
Silicon (Si), % | 0.2 to 0.5 | |
0 to 0.35 |
Sulfur (S), % | 0 to 0.010 | |
0 to 0.020 |
Titanium (Ti), % | 0 to 0.010 | |
0 to 0.040 |
Vanadium (V), % | 0.18 to 0.25 | |
0 to 0.020 |
Zirconium (Zr), % | 0 to 0.010 | |
0 |