EN 1.7376 Steel vs. Solder Alloy 133

EN 1.7376 steel belongs to the iron alloys classification, while solder alloy 133 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.7376 steel and the bottom bar is solder alloy 133.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
33
Elongation at Break, % 20
34
Poisson's Ratio 0.28
0.4
Shear Modulus, GPa 75
12
Tensile Strength: Ultimate (UTS), MPa 710
41

Thermal Properties

Latent Heat of Fusion, J/g 270
42
Melting Completion (Liquidus), °C 1460
220
Melting Onset (Solidus), °C 1410
180
Specific Heat Capacity, J/kg-K 470
180
Thermal Conductivity, W/m-K 26
47
Thermal Expansion, µm/m-K 13
25

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.2
11
Electrical Conductivity: Equal Weight (Specific), % IACS 11
10

Otherwise Unclassified Properties

Density, g/cm3 7.8
9.3
Embodied Carbon, kg CO2/kg material 2.1
9.4
Embodied Energy, MJ/kg 29
160
Embodied Water, L/kg 88
840

Common Calculations

Stiffness to Weight: Axial, points 14
2.0
Stiffness to Weight: Bending, points 25
12
Strength to Weight: Axial, points 25
1.2
Strength to Weight: Bending, points 23
2.9
Thermal Diffusivity, mm2/s 6.9
29
Thermal Shock Resistance, points 20
3.5

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0.2 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0.12 to 0.19
0
Chromium (Cr), % 8.0 to 10
0
Copper (Cu), % 0 to 0.3
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 86.2 to 90.6
0 to 0.020
Lead (Pb), % 0
48.5 to 50.3
Manganese (Mn), % 0.35 to 0.65
0
Molybdenum (Mo), % 0.9 to 1.2
0
Nickel (Ni), % 0 to 0.4
0 to 0.010
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
49.5 to 50.5
Vanadium (V), % 0 to 0.050
0
Zinc (Zn), % 0
0 to 0.0010