EN 1.7710 Steel vs. C11600 Copper
EN 1.7710 steel belongs to the iron alloys classification, while C11600 copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.7710 steel and the bottom bar is C11600 copper.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
120 |
Elongation at Break, % | 6.8 to 11 | |
2.7 to 50 |
Poisson's Ratio | 0.29 | |
0.34 |
Shear Modulus, GPa | 73 | |
43 |
Tensile Strength: Ultimate (UTS), MPa | 930 to 1070 | |
230 to 410 |
Tensile Strength: Yield (Proof), MPa | 800 to 1060 | |
77 to 410 |
Thermal Properties
Latent Heat of Fusion, J/g | 260 | |
210 |
Maximum Temperature: Mechanical, °C | 440 | |
200 |
Melting Completion (Liquidus), °C | 1470 | |
1080 |
Melting Onset (Solidus), °C | 1430 | |
1030 |
Specific Heat Capacity, J/kg-K | 470 | |
390 |
Thermal Conductivity, W/m-K | 41 | |
390 |
Thermal Expansion, µm/m-K | 13 | |
17 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
100 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
100 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 3.5 | |
35 |
Density, g/cm3 | 7.8 | |
9.0 |
Embodied Carbon, kg CO2/kg material | 2.2 | |
2.7 |
Embodied Energy, MJ/kg | 30 | |
42 |
Embodied Water, L/kg | 57 | |
390 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 73 to 100 | |
9.7 to 91 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 1680 to 2970 | |
25 to 710 |
Stiffness to Weight: Axial, points | 13 | |
7.2 |
Stiffness to Weight: Bending, points | 24 | |
18 |
Strength to Weight: Axial, points | 33 to 38 | |
7.2 to 13 |
Strength to Weight: Bending, points | 27 to 30 | |
9.4 to 14 |
Thermal Diffusivity, mm2/s | 11 | |
110 |
Thermal Shock Resistance, points | 27 to 31 | |
8.2 to 15 |
Alloy Composition
Carbon (C), % | 0.12 to 0.18 | |
0 |
Chromium (Cr), % | 1.3 to 1.8 | |
0 |
Copper (Cu), % | 0 | |
99.78 to 99.915 |
Iron (Fe), % | 95.1 to 97 | |
0 |
Manganese (Mn), % | 0.6 to 1.0 | |
0 |
Molybdenum (Mo), % | 0.8 to 1.0 | |
0 |
Phosphorus (P), % | 0 to 0.025 | |
0 |
Silicon (Si), % | 0 to 0.6 | |
0 |
Silver (Ag), % | 0 | |
0.085 to 0.12 |
Sulfur (S), % | 0 to 0.030 | |
0 |
Vanadium (V), % | 0.15 to 0.25 | |
0 |
Residuals, % | 0 | |
0 to 0.1 |