EN 1.8523 Steel vs. Nickel 690

EN 1.8523 steel belongs to the iron alloys classification, while nickel 690 belongs to the nickel alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.8523 steel and the bottom bar is nickel 690.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 300
90
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 15
3.4 to 34
Fatigue Strength, MPa 530
180 to 300
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
79
Shear Strength, MPa 610
420 to 570
Tensile Strength: Ultimate (UTS), MPa 1000
640 to 990
Tensile Strength: Yield (Proof), MPa 800
250 to 760

Thermal Properties

Latent Heat of Fusion, J/g 260
320
Maximum Temperature: Mechanical, °C 480
1010
Melting Completion (Liquidus), °C 1460
1380
Melting Onset (Solidus), °C 1420
1340
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
14
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 9.0
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 4.2
50
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 2.2
8.2
Embodied Energy, MJ/kg 31
120
Embodied Water, L/kg 64
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
31 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 1700
160 to 1440
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 36
21 to 33
Strength to Weight: Bending, points 28
20 to 27
Thermal Diffusivity, mm2/s 10
3.5
Thermal Shock Resistance, points 29
16 to 25

Alloy Composition

Carbon (C), % 0.35 to 0.45
0 to 0.050
Chromium (Cr), % 3.0 to 3.5
27 to 31
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 93.5 to 95.7
7.0 to 11
Manganese (Mn), % 0.4 to 0.7
0 to 0.5
Molybdenum (Mo), % 0.8 to 1.1
0
Nickel (Ni), % 0
58 to 66
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 0.4
0 to 0.5
Sulfur (S), % 0 to 0.035
0 to 0.015
Vanadium (V), % 0.15 to 0.25
0