MakeItFrom.com
Menu (ESC)

EN 1.8879 Steel vs. EN 1.8831 Steel

Both EN 1.8879 steel and EN 1.8831 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.8879 steel and the bottom bar is EN 1.8831 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 16
19
Fatigue Strength, MPa 460
330
Impact Strength: V-Notched Charpy, J 67
110
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 510
390
Tensile Strength: Ultimate (UTS), MPa 830
630
Tensile Strength: Yield (Proof), MPa 710
480

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
49
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.1
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 9.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 3.7
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.6
Embodied Energy, MJ/kg 26
21
Embodied Water, L/kg 54
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
110
Resilience: Unit (Modulus of Resilience), kJ/m3 1320
620
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 29
22
Strength to Weight: Bending, points 25
21
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 24
18

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.040
Boron (B), % 0 to 0.0050
0
Carbon (C), % 0 to 0.2
0 to 0.16
Chromium (Cr), % 0 to 1.5
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 91.9 to 100
96.6 to 99.98
Manganese (Mn), % 0 to 1.7
0 to 1.7
Molybdenum (Mo), % 0 to 0.7
0 to 0.2
Nickel (Ni), % 0 to 2.5
0 to 0.5
Niobium (Nb), % 0 to 0.060
0 to 0.050
Nitrogen (N), % 0 to 0.015
0 to 0.020
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.8
0 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.0050
Titanium (Ti), % 0 to 0.050
0 to 0.050
Vanadium (V), % 0 to 0.12
0 to 0.1
Zirconium (Zr), % 0 to 0.15
0