EN 1.8903 Steel vs. S35135 Stainless Steel

Both EN 1.8903 steel and S35135 stainless steel are iron alloys. They have a modest 39% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.8903 steel and the bottom bar is S35135 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
34
Fatigue Strength, MPa 330
180
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
79
Shear Strength, MPa 390
390
Tensile Strength: Ultimate (UTS), MPa 630
590
Tensile Strength: Yield (Proof), MPa 480
230

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 410
1100
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Expansion, µm/m-K 13
16

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
37
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.8
6.8
Embodied Energy, MJ/kg 24
94
Embodied Water, L/kg 51
220

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
160
Resilience: Unit (Modulus of Resilience), kJ/m3 620
130
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
20
Strength to Weight: Bending, points 21
19
Thermal Shock Resistance, points 18
13

Alloy Composition

Aluminum (Al), % 0 to 0.015
0
Carbon (C), % 0 to 0.22
0 to 0.080
Chromium (Cr), % 0 to 0.35
20 to 25
Copper (Cu), % 0 to 0.6
0 to 0.75
Iron (Fe), % 95 to 99.05
28.3 to 45
Manganese (Mn), % 1.0 to 1.8
0 to 1.0
Molybdenum (Mo), % 0 to 0.13
4.0 to 4.8
Nickel (Ni), % 0 to 0.85
30 to 38
Niobium (Nb), % 0 to 0.060
0
Nitrogen (N), % 0 to 0.027
0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.65
0.6 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015
Titanium (Ti), % 0 to 0.060
0.4 to 1.0
Vanadium (V), % 0 to 0.22
0