EN 1.8965 Steel vs. SAE-AISI 1095 Steel

Both EN 1.8965 steel and SAE-AISI 1095 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.8965 steel and the bottom bar is SAE-AISI 1095 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
200 to 270
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 16
10 to 11
Fatigue Strength, MPa 220
310 to 370
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Shear Strength, MPa 350
400 to 540
Tensile Strength: Ultimate (UTS), MPa 570
680 to 900
Tensile Strength: Yield (Proof), MPa 340
500 to 590

Thermal Properties

Latent Heat of Fusion, J/g 250
240
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
47
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
9.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
11

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.8
1.4
Embodied Energy, MJ/kg 25
19
Embodied Water, L/kg 52
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78
63 to 84
Resilience: Unit (Modulus of Resilience), kJ/m3 300
660 to 930
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
24 to 32
Strength to Weight: Bending, points 19
22 to 26
Thermal Diffusivity, mm2/s 10
13
Thermal Shock Resistance, points 17
22 to 29

Alloy Composition

Aluminum (Al), % 0 to 0.030
0
Carbon (C), % 0 to 0.19
0.9 to 1.0
Chromium (Cr), % 0.35 to 0.85
0
Copper (Cu), % 0.2 to 0.6
0
Iron (Fe), % 94.6 to 99
98.4 to 98.8
Manganese (Mn), % 0.45 to 1.6
0.3 to 0.5
Molybdenum (Mo), % 0 to 0.35
0
Nickel (Ni), % 0 to 0.7
0
Niobium (Nb), % 0 to 0.065
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.55
0
Sulfur (S), % 0 to 0.035
0 to 0.050
Titanium (Ti), % 0 to 0.12
0
Vanadium (V), % 0 to 0.14
0
Zirconium (Zr), % 0 to 0.17
0