EN 2.4815 Cast Nickel vs. SAE-AISI 1095 Steel

EN 2.4815 cast nickel belongs to the nickel alloys classification, while SAE-AISI 1095 steel belongs to the iron alloys. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 2.4815 cast nickel and the bottom bar is SAE-AISI 1095 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 3.4
10 to 11
Fatigue Strength, MPa 89
310 to 370
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
72
Tensile Strength: Ultimate (UTS), MPa 460
680 to 900
Tensile Strength: Yield (Proof), MPa 220
500 to 590

Thermal Properties

Latent Heat of Fusion, J/g 330
240
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1510
1450
Melting Onset (Solidus), °C 1450
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 25
47
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.1
9.6
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
11

Otherwise Unclassified Properties

Base Metal Price, % relative 47
1.8
Density, g/cm3 8.3
7.8
Embodied Carbon, kg CO2/kg material 7.9
1.4
Embodied Energy, MJ/kg 110
19
Embodied Water, L/kg 230
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 13
63 to 84
Resilience: Unit (Modulus of Resilience), kJ/m3 130
660 to 930
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 15
24 to 32
Strength to Weight: Bending, points 16
22 to 26
Thermal Diffusivity, mm2/s 6.4
13
Thermal Shock Resistance, points 17
22 to 29

Alloy Composition

Carbon (C), % 0.35 to 0.65
0.9 to 1.0
Chromium (Cr), % 12 to 18
0
Iron (Fe), % 9.8 to 28.7
98.4 to 98.8
Manganese (Mn), % 0 to 2.0
0.3 to 0.5
Molybdenum (Mo), % 0 to 1.0
0
Nickel (Ni), % 58 to 66
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0
Sulfur (S), % 0 to 0.030
0 to 0.050