CC497K Bronze vs. ACI-ASTM CK3MCuN Steel
CC497K bronze belongs to the copper alloys classification, while ACI-ASTM CK3MCuN steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is CC497K bronze and the bottom bar is ACI-ASTM CK3MCuN steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 55 | |
| 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 93 | |
| 200 |
| Elongation at Break, % | 6.7 | |
| 39 |
| Poisson's Ratio | 0.36 | |
| 0.28 |
| Shear Modulus, GPa | 34 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 190 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 91 | |
| 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 160 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 1090 |
| Melting Completion (Liquidus), °C | 870 | |
| 1460 |
| Melting Onset (Solidus), °C | 800 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 330 | |
| 460 |
| Thermal Conductivity, W/m-K | 53 | |
| 12 |
| Thermal Expansion, µm/m-K | 20 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 1.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.7 | |
| 2.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 29 |
| Density, g/cm3 | 9.3 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 5.6 |
| Embodied Energy, MJ/kg | 48 | |
| 76 |
| Embodied Water, L/kg | 370 | |
| 190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 10 | |
| 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 45 | |
| 210 |
| Stiffness to Weight: Axial, points | 5.5 | |
| 14 |
| Stiffness to Weight: Bending, points | 16 | |
| 24 |
| Strength to Weight: Axial, points | 5.6 | |
| 21 |
| Strength to Weight: Bending, points | 7.8 | |
| 20 |
| Thermal Diffusivity, mm2/s | 17 | |
| 3.2 |
| Thermal Shock Resistance, points | 7.2 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.75 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.025 |
| Chromium (Cr), % | 0 | |
| 19.5 to 20.5 |
| Copper (Cu), % | 67.5 to 77.5 | |
| 0.5 to 1.0 |
| Iron (Fe), % | 0 to 0.25 | |
| 49.5 to 56.3 |
| Lead (Pb), % | 18 to 23 | |
| 0 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 to 1.2 |
| Molybdenum (Mo), % | 0 | |
| 6.0 to 7.0 |
| Nickel (Ni), % | 0.5 to 2.5 | |
| 17.5 to 19.5 |
| Nitrogen (N), % | 0 | |
| 0.18 to 0.24 |
| Phosphorus (P), % | 0 to 0.1 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.1 | |
| 0 to 0.010 |
| Tin (Sn), % | 4.0 to 6.0 | |
| 0 |
| Zinc (Zn), % | 0 to 2.0 | |
| 0 |