Full-hard Nickel 201 vs. Full-hard Type 2 Magnetic Alloy
Full-hard nickel 201 belongs to the nickel alloys classification, while full-hard Type 2 magnetic alloy belongs to the iron alloys. They have 49% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is full-hard nickel 201 and the bottom bar is full-hard Type 2 magnetic alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 190 |
| Elongation at Break, % | 4.5 | |
| 2.0 |
| Poisson's Ratio | 0.31 | |
| 0.3 |
| Shear Modulus, GPa | 70 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 660 | |
| 910 |
| Tensile Strength: Yield (Proof), MPa | 510 | |
| 870 |
Thermal Properties
| Curie Temperature, °C | 360 | |
| 480 |
| Latent Heat of Fusion, J/g | 290 | |
| 270 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1420 |
| Melting Onset (Solidus), °C | 1440 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 460 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 19 | |
| 3.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 19 | |
| 4.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 65 | |
| 33 |
| Density, g/cm3 | 8.9 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 5.9 |
| Embodied Energy, MJ/kg | 150 | |
| 81 |
| Embodied Water, L/kg | 230 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 27 | |
| 18 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 720 | |
| 2010 |
| Stiffness to Weight: Axial, points | 11 | |
| 12 |
| Stiffness to Weight: Bending, points | 21 | |
| 23 |
| Strength to Weight: Axial, points | 20 | |
| 30 |
| Strength to Weight: Bending, points | 19 | |
| 25 |
| Thermal Shock Resistance, points | 19 | |
| 29 |
Alloy Composition
| Carbon (C), % | 0 to 0.020 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 0 to 0.3 |
| Cobalt (Co), % | 0 | |
| 0 to 0.5 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 to 0.4 | |
| 48.2 to 53 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.3 |
| Nickel (Ni), % | 99 to 100 | |
| 47 to 49 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |