Grade 2 Babbitt Metal vs. S21600 Stainless Steel
Grade 2 Babbitt Metal belongs to the otherwise unclassified metals classification, while S21600 stainless steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is grade 2 Babbitt Metal and the bottom bar is S21600 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 25 | |
200 |
Elastic (Young's, Tensile) Modulus, GPa | 53 | |
200 |
Poisson's Ratio | 0.35 | |
0.28 |
Shear Modulus, GPa | 19 | |
79 |
Tensile Strength: Yield (Proof), MPa | 42 | |
390 |
Thermal Properties
Latent Heat of Fusion, J/g | 72 | |
290 |
Melting Completion (Liquidus), °C | 350 | |
1420 |
Melting Onset (Solidus), °C | 240 | |
1380 |
Specific Heat Capacity, J/kg-K | 230 | |
480 |
Thermal Expansion, µm/m-K | 21 | |
17 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 70 | |
17 |
Density, g/cm3 | 7.3 | |
7.7 |
Embodied Carbon, kg CO2/kg material | 12 | |
3.6 |
Embodied Energy, MJ/kg | 200 | |
50 |
Embodied Water, L/kg | 1240 | |
160 |
Common Calculations
Resilience: Unit (Modulus of Resilience), kJ/m3 | 17 | |
370 |
Stiffness to Weight: Axial, points | 4.0 | |
14 |
Stiffness to Weight: Bending, points | 17 | |
25 |
Alloy Composition
Aluminum (Al), % | 0 to 0.0050 | |
0 |
Antimony (Sb), % | 7.0 to 8.0 | |
0 |
Arsenic (As), % | 0 to 0.1 | |
0 |
Bismuth (Bi), % | 0 to 0.080 | |
0 |
Cadmium (Cd), % | 0 to 0.050 | |
0 |
Carbon (C), % | 0 | |
0 to 0.080 |
Chromium (Cr), % | 0 | |
17.5 to 22 |
Copper (Cu), % | 3.0 to 4.0 | |
0 |
Iron (Fe), % | 0 to 0.080 | |
57.6 to 67.8 |
Lead (Pb), % | 0 to 0.35 | |
0 |
Manganese (Mn), % | 0 | |
7.5 to 9.0 |
Molybdenum (Mo), % | 0 | |
2.0 to 3.0 |
Nickel (Ni), % | 0 | |
5.0 to 7.0 |
Nitrogen (N), % | 0 | |
0.25 to 0.5 |
Phosphorus (P), % | 0 | |
0 to 0.045 |
Silicon (Si), % | 0 | |
0 to 0.75 |
Sulfur (S), % | 0 | |
0 to 0.030 |
Tin (Sn), % | 87.3 to 90 | |
0 |
Zinc (Zn), % | 0 to 0.0050 | |
0 |