Grade 250 Maraging Steel vs. R30605 Cobalt
Grade 250 maraging steel belongs to the iron alloys classification, while R30605 cobalt belongs to the cobalt alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is grade 250 maraging steel and the bottom bar is R30605 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 7.3 to 17 | |
| 34 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 970 to 1800 | |
| 1130 to 1900 |
| Tensile Strength: Yield (Proof), MPa | 660 to 1740 | |
| 470 to 1600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 290 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1410 |
| Melting Onset (Solidus), °C | 1430 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 410 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 9.6 |
| Embodied Carbon, kg CO2/kg material | 4.9 | |
| 9.8 |
| Embodied Energy, MJ/kg | 65 | |
| 140 |
| Embodied Water, L/kg | 140 | |
| 450 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 12 |
| Stiffness to Weight: Bending, points | 23 | |
| 21 |
| Strength to Weight: Axial, points | 33 to 61 | |
| 33 to 55 |
| Strength to Weight: Bending, points | 26 to 40 | |
| 25 to 36 |
| Thermal Shock Resistance, points | 29 to 54 | |
| 31 to 52 |
Alloy Composition
| Aluminum (Al), % | 0.050 to 0.15 | |
| 0 |
| Boron (B), % | 0 to 0.0030 | |
| 0 |
| Calcium (Ca), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 0 | |
| 19 to 21 |
| Cobalt (Co), % | 7.0 to 8.5 | |
| 46.4 to 57 |
| Iron (Fe), % | 66.3 to 71.1 | |
| 0 to 3.0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 1.0 to 2.0 |
| Molybdenum (Mo), % | 4.6 to 5.2 | |
| 0 |
| Nickel (Ni), % | 17 to 19 | |
| 9.0 to 11 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0.3 to 0.5 | |
| 0 |
| Tungsten (W), % | 0 | |
| 14 to 16 |
| Zirconium (Zr), % | 0 to 0.020 | |
| 0 |