Grade 364 Molybdenum vs. C71000 Copper-nickel
Grade 364 molybdenum belongs to the otherwise unclassified metals classification, while C71000 copper-nickel belongs to the copper alloys. There are 16 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is grade 364 molybdenum and the bottom bar is C71000 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 310 | |
| 130 |
| Poisson's Ratio | 0.31 | |
| 0.33 |
| Shear Modulus, GPa | 120 | |
| 49 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 720 | |
| 320 to 560 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 230 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 400 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 28 | |
| 4.3 |
| Embodied Energy, MJ/kg | 330 | |
| 63 |
| Embodied Water, L/kg | 360 | |
| 290 |
Common Calculations
| Stiffness to Weight: Axial, points | 17 | |
| 8.2 |
| Stiffness to Weight: Bending, points | 22 | |
| 19 |
| Strength to Weight: Axial, points | 16 to 20 | |
| 10 to 18 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 12 to 17 |
| Thermal Shock Resistance, points | 19 to 24 | |
| 12 to 20 |
Alloy Composition
| Carbon (C), % | 0.010 to 0.040 | |
| 0 |
| Copper (Cu), % | 0 | |
| 73.5 to 80.5 |
| Iron (Fe), % | 0 to 0.010 | |
| 0.5 to 1.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 99.2 to 99.5 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 19 to 23 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 |
| Oxygen (O), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 |
| Titanium (Ti), % | 0.4 to 0.55 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Zirconium (Zr), % | 0.060 to 0.12 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |