Grade 364 Molybdenum vs. K93600 Alloy
Grade 364 molybdenum belongs to the otherwise unclassified metals classification, while K93600 alloy belongs to the iron alloys. There are 14 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is grade 364 molybdenum and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 310 | |
| 140 |
| Elongation at Break, % | 6.2 to 11 | |
| 5.0 to 35 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 720 | |
| 480 to 810 |
| Tensile Strength: Yield (Proof), MPa | 350 to 620 | |
| 280 to 750 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 250 | |
| 520 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 7.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.1 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 43 to 57 | |
| 21 to 280 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 630 | |
| 280 to 2050 |
| Stiffness to Weight: Axial, points | 17 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 22 | |
| 21 |
| Strength to Weight: Axial, points | 16 to 20 | |
| 16 to 28 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 17 to 24 |
| Thermal Shock Resistance, points | 19 to 24 | |
| 34 to 57 |