Grade 364 Molybdenum vs. Z41121 Zinc
Grade 364 molybdenum belongs to the otherwise unclassified metals classification, while Z41121 zinc belongs to the zinc alloys. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is grade 364 molybdenum and the bottom bar is Z41121 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 310 | |
| 87 |
| Elongation at Break, % | 6.2 to 11 | |
| 50 |
| Poisson's Ratio | 0.31 | |
| 0.25 |
| Shear Modulus, GPa | 120 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 720 | |
| 140 |
| Tensile Strength: Yield (Proof), MPa | 350 to 620 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 370 | |
| 110 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 390 |
| Thermal Expansion, µm/m-K | 7.0 | |
| 26 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 28 | |
| 2.8 |
| Embodied Energy, MJ/kg | 330 | |
| 54 |
| Embodied Water, L/kg | 360 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 43 to 57 | |
| 68 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 630 | |
| 79 |
| Stiffness to Weight: Axial, points | 17 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 22 | |
| 23 |
| Strength to Weight: Axial, points | 16 to 20 | |
| 6.1 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 9.3 |
| Thermal Shock Resistance, points | 19 to 24 | |
| 4.6 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.010 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Carbon (C), % | 0.010 to 0.040 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0.080 to 0.49 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.010 |
| Lead (Pb), % | 0 | |
| 0 to 0.010 |
| Molybdenum (Mo), % | 99.2 to 99.5 | |
| 0 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0 |
| Nitrogen (N), % | 0 to 0.0020 | |
| 0 |
| Oxygen (O), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Titanium (Ti), % | 0.4 to 0.55 | |
| 0.050 to 0.18 |
| Zinc (Zn), % | 0 | |
| 99.292 to 99.87 |
| Zirconium (Zr), % | 0.060 to 0.12 | |
| 0 |