Grade 365 Molybdenum vs. ASTM A356 Grade 10

Grade 365 molybdenum belongs to the otherwise unclassified metals classification, while ASTM A356 grade 10 belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is grade 365 molybdenum and the bottom bar is ASTM A356 grade 10.

Grade 365 Molybdenum ASTM A356 Grade 10 (J22090) Cast Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		310
Elastic (Young's, Tensile) Modulus, GPa		190

Elongation at Break, %		6.3
Elongation at Break, %		23

Poisson's Ratio		0.31
Poisson's Ratio		0.29

Shear Modulus, GPa		120
Shear Modulus, GPa		74

Tensile Strength: Ultimate (UTS), MPa		620
Tensile Strength: Ultimate (UTS), MPa		670

Tensile Strength: Yield (Proof), MPa		530
Tensile Strength: Yield (Proof), MPa		430

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		260

Specific Heat Capacity, J/kg-K		250
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		7.0
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Density, g/cm³		10
Density, g/cm³		7.9

Embodied Carbon, kg CO₂/kg material		28
Embodied Carbon, kg CO₂/kg material		1.8

Embodied Energy, MJ/kg		330
Embodied Energy, MJ/kg		23

Embodied Water, L/kg		360
Embodied Water, L/kg		59

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		37
Resilience: Ultimate (Unit Rupture Work), MJ/m³		130

Resilience: Unit (Modulus of Resilience), kJ/m³		450
Resilience: Unit (Modulus of Resilience), kJ/m³		480

Stiffness to Weight: Axial, points		17
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		22
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		17
Strength to Weight: Axial, points		24

Strength to Weight: Bending, points		16
Strength to Weight: Bending, points		22

Thermal Shock Resistance, points		21
Thermal Shock Resistance, points		19

Alloy Composition

Carbon (C), %		0 to 0.010
Carbon (C), %		0 to 0.2

Chromium (Cr), %		0
Chromium (Cr), %		2.0 to 2.8

Iron (Fe), %		0 to 0.010
Iron (Fe), %		94.4 to 96.6

Manganese (Mn), %		0
Manganese (Mn), %		0.5 to 0.8

Molybdenum (Mo), %		99.9 to 100
Molybdenum (Mo), %		0.9 to 1.2

Nickel (Ni), %		0 to 0.0020
Nickel (Ni), %		0

Nitrogen (N), %		0 to 0.0020
Nitrogen (N), %		0

Oxygen (O), %		0 to 0.0015
Oxygen (O), %		0

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.035

Silicon (Si), %		0 to 0.010
Silicon (Si), %		0 to 0.6

Sulfur (S), %		0
Sulfur (S), %		0 to 0.030