Grade 702C Zirconium vs. Grade Ti-Pd17 Titanium
Grade 702C zirconium belongs to the otherwise unclassified metals classification, while grade Ti-Pd17 titanium belongs to the titanium alloys. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is grade 702C zirconium and the bottom bar is grade Ti-Pd17 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 | |
| 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 97 | |
| 110 |
| Elongation at Break, % | 13 | |
| 22 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 36 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 270 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 420 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 540 |
| Thermal Conductivity, W/m-K | 22 | |
| 21 |
| Thermal Expansion, µm/m-K | 5.7 | |
| 8.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 4.5 |
| Embodied Water, L/kg | 450 | |
| 230 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 52 | |
| 55 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 510 | |
| 180 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 35 |
| Strength to Weight: Axial, points | 18 | |
| 17 |
| Strength to Weight: Bending, points | 19 | |
| 21 |
| Thermal Diffusivity, mm2/s | 12 | |
| 8.8 |
| Thermal Shock Resistance, points | 55 | |
| 21 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.1 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 | |
| 0 to 0.030 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.25 | |
| 0 to 0.25 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 98.9 to 99.96 |
| Zirconium (Zr), % | 94.8 to 100 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |