Grade 702C Zirconium vs. SAE-AISI 1146 Steel
Grade 702C zirconium belongs to the otherwise unclassified metals classification, while SAE-AISI 1146 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is grade 702C zirconium and the bottom bar is SAE-AISI 1146 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 | |
| 190 to 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 97 | |
| 190 |
| Elongation at Break, % | 13 | |
| 13 to 17 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 36 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 670 to 730 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 360 to 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 470 |
| Thermal Conductivity, W/m-K | 22 | |
| 51 |
| Thermal Expansion, µm/m-K | 5.7 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 7.8 |
| Embodied Water, L/kg | 450 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 52 | |
| 93 to 97 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 510 | |
| 340 to 1050 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 18 | |
| 24 to 26 |
| Strength to Weight: Bending, points | 19 | |
| 22 to 23 |
| Thermal Diffusivity, mm2/s | 12 | |
| 14 |
| Thermal Shock Resistance, points | 55 | |
| 20 to 22 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 0.42 to 0.49 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 98.3 to 98.8 |
| Manganese (Mn), % | 0 | |
| 0.7 to 1.0 |
| Nitrogen (N), % | 0 to 0.030 | |
| 0 |
| Oxygen (O), % | 0 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.040 |
| Sulfur (S), % | 0 | |
| 0.080 to 0.13 |
| Zirconium (Zr), % | 94.8 to 100 | |
| 0 |