Grade 9 Titanium vs. Z24311 Zinc

Grade 9 titanium belongs to the titanium alloys classification, while Z24311 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is grade 9 titanium and the bottom bar is Z24311 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
87
Elongation at Break, % 11 to 17
63
Poisson's Ratio 0.32
0.25
Shear Modulus, GPa 40
35
Tensile Strength: Ultimate (UTS), MPa 700 to 960
140
Tensile Strength: Yield (Proof), MPa 540 to 830
120

Thermal Properties

Latent Heat of Fusion, J/g 410
110
Maximum Temperature: Mechanical, °C 330
90
Melting Completion (Liquidus), °C 1640
410
Melting Onset (Solidus), °C 1590
400
Specific Heat Capacity, J/kg-K 550
390
Thermal Conductivity, W/m-K 8.1
110
Thermal Expansion, µm/m-K 9.1
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
27
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
37

Otherwise Unclassified Properties

Base Metal Price, % relative 37
11
Density, g/cm3 4.5
6.6
Embodied Carbon, kg CO2/kg material 36
2.8
Embodied Energy, MJ/kg 580
53
Embodied Water, L/kg 150
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 89 to 110
85
Resilience: Unit (Modulus of Resilience), kJ/m3 1380 to 3220
81
Stiffness to Weight: Axial, points 13
7.4
Stiffness to Weight: Bending, points 35
23
Strength to Weight: Axial, points 43 to 60
6.1
Strength to Weight: Bending, points 39 to 48
9.3
Thermal Diffusivity, mm2/s 3.3
44
Thermal Shock Resistance, points 52 to 71
4.6

Alloy Composition

Aluminum (Al), % 2.5 to 3.5
0 to 0.0020
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.080
0
Copper (Cu), % 0
0 to 0.0050
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0 to 0.25
0 to 0.010
Lead (Pb), % 0
0.030 to 0.080
Magnesium (Mg), % 0
0 to 0.0015
Manganese (Mn), % 0
0 to 0.015
Nitrogen (N), % 0 to 0.030
0
Oxygen (O), % 0 to 0.15
0
Titanium (Ti), % 92.6 to 95.5
0 to 0.020
Vanadium (V), % 2.0 to 3.0
0
Zinc (Zn), % 0
99.862 to 100
Residuals, % 0 to 0.4
0