Grade TDSiCr Steel vs. S46910 Stainless Steel
Both grade TDSiCr steel and S46910 stainless steel are iron alloys. They have 72% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is grade TDSiCr steel and the bottom bar is S46910 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 590 | |
| 270 to 630 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 80 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 1950 | |
| 680 to 2470 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 810 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.2 | |
| 18 |
| Density, g/cm3 | 7.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 4.1 |
| Embodied Energy, MJ/kg | 20 | |
| 55 |
| Embodied Water, L/kg | 48 | |
| 140 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 70 | |
| 24 to 86 |
| Strength to Weight: Bending, points | 45 | |
| 22 to 51 |
| Thermal Shock Resistance, points | 58 | |
| 23 to 84 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.15 to 0.5 |
| Carbon (C), % | 0.5 to 0.6 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0.5 to 0.8 | |
| 11 to 13 |
| Copper (Cu), % | 0 to 0.1 | |
| 1.5 to 3.5 |
| Iron (Fe), % | 96.6 to 97.8 | |
| 65 to 76 |
| Manganese (Mn), % | 0.5 to 0.9 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 3.0 to 5.0 |
| Nickel (Ni), % | 0 | |
| 8.0 to 10 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.030 |
| Silicon (Si), % | 1.2 to 1.6 | |
| 0 to 0.7 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0.5 to 1.2 |