Grade VDSiCr Steel vs. EN 1.8523 Steel
Both grade VDSiCr steel and EN 1.8523 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is grade VDSiCr steel and the bottom bar is EN 1.8523 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 590 | |
| 300 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 80 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 1950 | |
| 1000 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 480 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 46 | |
| 39 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 7.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 9.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.2 | |
| 4.2 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 2.2 |
| Embodied Energy, MJ/kg | 20 | |
| 31 |
| Embodied Water, L/kg | 48 | |
| 64 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 70 | |
| 36 |
| Strength to Weight: Bending, points | 45 | |
| 28 |
| Thermal Diffusivity, mm2/s | 12 | |
| 10 |
| Thermal Shock Resistance, points | 58 | |
| 29 |
Alloy Composition
| Carbon (C), % | 0.5 to 0.6 | |
| 0.35 to 0.45 |
| Chromium (Cr), % | 0.5 to 0.8 | |
| 3.0 to 3.5 |
| Copper (Cu), % | 0 to 0.060 | |
| 0 |
| Iron (Fe), % | 96.6 to 97.8 | |
| 93.5 to 95.7 |
| Manganese (Mn), % | 0.5 to 0.9 | |
| 0.4 to 0.7 |
| Molybdenum (Mo), % | 0 | |
| 0.8 to 1.1 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.035 |
| Silicon (Si), % | 1.2 to 1.6 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.035 |
| Vanadium (V), % | 0 | |
| 0.15 to 0.25 |