Solder Alloy 133 vs. C55284 Copper
Solder alloy 133 belongs to the otherwise unclassified metals classification, while C55284 copper belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is solder alloy 133 and the bottom bar is C55284 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 33 | |
| 100 |
| Poisson's Ratio | 0.4 | |
| 0.34 |
| Shear Modulus, GPa | 12 | |
| 38 |
| Tensile Strength: Ultimate (UTS), MPa | 41 | |
| 180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 42 | |
| 180 |
| Melting Completion (Liquidus), °C | 220 | |
| 800 |
| Melting Onset (Solidus), °C | 180 | |
| 640 |
| Specific Heat Capacity, J/kg-K | 180 | |
| 380 |
| Thermal Expansion, µm/m-K | 25 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.3 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 9.4 | |
| 16 |
| Embodied Energy, MJ/kg | 160 | |
| 260 |
Common Calculations
| Stiffness to Weight: Axial, points | 2.0 | |
| 6.5 |
| Stiffness to Weight: Bending, points | 12 | |
| 18 |
| Strength to Weight: Axial, points | 1.2 | |
| 5.6 |
| Strength to Weight: Bending, points | 2.9 | |
| 8.0 |
| Thermal Shock Resistance, points | 3.5 | |
| 7.4 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 0.2 to 0.5 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Copper (Cu), % | 0 to 0.080 | |
| 79.2 to 80.7 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 |
| Lead (Pb), % | 48.5 to 50.3 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 4.8 to 5.2 |
| Silver (Ag), % | 0 to 0.1 | |
| 14.5 to 15.5 |
| Tin (Sn), % | 49.5 to 50.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |