Solder Alloy 133 vs. N06230 Nickel
Solder alloy 133 belongs to the otherwise unclassified metals classification, while N06230 nickel belongs to the nickel alloys. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is solder alloy 133 and the bottom bar is N06230 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 33 | |
| 210 |
| Elongation at Break, % | 34 | |
| 38 to 48 |
| Poisson's Ratio | 0.4 | |
| 0.28 |
| Shear Modulus, GPa | 12 | |
| 83 |
| Tensile Strength: Ultimate (UTS), MPa | 41 | |
| 620 to 840 |
Thermal Properties
| Latent Heat of Fusion, J/g | 42 | |
| 310 |
| Melting Completion (Liquidus), °C | 220 | |
| 1370 |
| Melting Onset (Solidus), °C | 180 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 180 | |
| 420 |
| Thermal Conductivity, W/m-K | 47 | |
| 8.9 |
| Thermal Expansion, µm/m-K | 25 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 1.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 1.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.3 | |
| 9.5 |
| Embodied Carbon, kg CO2/kg material | 9.4 | |
| 11 |
| Embodied Energy, MJ/kg | 160 | |
| 160 |
| Embodied Water, L/kg | 840 | |
| 290 |
Common Calculations
| Stiffness to Weight: Axial, points | 2.0 | |
| 12 |
| Stiffness to Weight: Bending, points | 12 | |
| 21 |
| Strength to Weight: Axial, points | 1.2 | |
| 18 to 25 |
| Strength to Weight: Bending, points | 2.9 | |
| 17 to 21 |
| Thermal Diffusivity, mm2/s | 29 | |
| 2.3 |
| Thermal Shock Resistance, points | 3.5 | |
| 17 to 23 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0.2 to 0.5 |
| Antimony (Sb), % | 0.2 to 0.5 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Boron (B), % | 0 | |
| 0 to 0.015 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 0 | |
| 20 to 24 |
| Cobalt (Co), % | 0 | |
| 0 to 5.0 |
| Copper (Cu), % | 0 to 0.080 | |
| 0 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 to 3.0 |
| Lanthanum (La), % | 0 | |
| 0.0050 to 0.050 |
| Lead (Pb), % | 48.5 to 50.3 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.3 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 1.0 to 3.0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 47.5 to 65.2 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.25 to 0.75 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tin (Sn), % | 49.5 to 50.5 | |
| 0 |
| Tungsten (W), % | 0 | |
| 13 to 15 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |