Monel 400 vs. AISI 410 Stainless Steel
Monel 400 belongs to the nickel alloys classification, while AISI 410 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is Monel 400 and the bottom bar is AISI 410 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 160 | |
| 190 |
| Elongation at Break, % | 20 to 40 | |
| 16 to 22 |
| Fatigue Strength, MPa | 230 to 290 | |
| 190 to 350 |
| Poisson's Ratio | 0.32 | |
| 0.28 |
| Shear Modulus, GPa | 62 | |
| 76 |
| Shear Strength, MPa | 370 to 490 | |
| 330 to 470 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 780 | |
| 520 to 770 |
| Tensile Strength: Yield (Proof), MPa | 210 to 590 | |
| 290 to 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 1000 | |
| 710 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1530 |
| Melting Onset (Solidus), °C | 1300 | |
| 1480 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 480 |
| Thermal Conductivity, W/m-K | 23 | |
| 30 |
| Thermal Expansion, µm/m-K | 14 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.3 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.4 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 50 | |
| 7.0 |
| Calomel Potential, mV | -80 | |
| -150 |
| Density, g/cm3 | 8.9 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 1.9 |
| Embodied Energy, MJ/kg | 110 | |
| 27 |
| Embodied Water, L/kg | 250 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 180 | |
| 97 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 1080 | |
| 210 to 860 |
| Stiffness to Weight: Axial, points | 10 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 25 |
| Strength to Weight: Axial, points | 17 to 25 | |
| 19 to 28 |
| Strength to Weight: Bending, points | 17 to 21 | |
| 19 to 24 |
| Thermal Diffusivity, mm2/s | 6.1 | |
| 8.1 |
| Thermal Shock Resistance, points | 17 to 25 | |
| 18 to 26 |
Alloy Composition
| Carbon (C), % | 0 to 0.3 | |
| 0.080 to 0.15 |
| Chromium (Cr), % | 0 | |
| 11.5 to 13.5 |
| Copper (Cu), % | 28 to 34 | |
| 0 |
| Iron (Fe), % | 0 to 2.5 | |
| 83.5 to 88.4 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 63 to 72 | |
| 0 to 0.75 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.024 | |
| 0 to 0.030 |