MakeItFrom.com
Menu (ESC)

Monel 400 vs. Monel R-405

Both Monel 400 and Monel R-405 are nickel alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is Monel 400 and the bottom bar is Monel R-405.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 160
160
Elongation at Break, % 20 to 40
9.1 to 39
Fatigue Strength, MPa 230 to 290
210 to 250
Poisson's Ratio 0.32
0.32
Shear Modulus, GPa 62
62
Shear Strength, MPa 370 to 490
350 to 370
Tensile Strength: Ultimate (UTS), MPa 540 to 780
540 to 630
Tensile Strength: Yield (Proof), MPa 210 to 590
190 to 350

Thermal Properties

Curie Temperature, °C 40
18
Latent Heat of Fusion, J/g 270
270
Maximum Temperature: Mechanical, °C 1000
900
Melting Completion (Liquidus), °C 1350
1350
Melting Onset (Solidus), °C 1300
1300
Specific Heat Capacity, J/kg-K 430
430
Thermal Conductivity, W/m-K 23
23
Thermal Expansion, µm/m-K 14
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.3
3.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 50
50
Density, g/cm3 8.9
8.9
Embodied Carbon, kg CO2/kg material 7.9
7.9
Embodied Energy, MJ/kg 110
110
Embodied Water, L/kg 250
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 180
49 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 1080
120 to 370
Stiffness to Weight: Axial, points 10
10
Stiffness to Weight: Bending, points 21
21
Strength to Weight: Axial, points 17 to 25
17 to 20
Strength to Weight: Bending, points 17 to 21
17 to 18
Thermal Diffusivity, mm2/s 6.1
5.9
Thermal Shock Resistance, points 17 to 25
17 to 20

Alloy Composition

Carbon (C), % 0 to 0.3
0 to 0.3
Copper (Cu), % 28 to 34
28 to 34
Iron (Fe), % 0 to 2.5
0 to 2.5
Manganese (Mn), % 0 to 2.0
0 to 2.0
Nickel (Ni), % 63 to 72
63 to 72
Silicon (Si), % 0 to 0.5
0 to 0.5
Sulfur (S), % 0 to 0.024
0.025 to 0.060

Comparable Variants