Monel 400 vs. Nickel Beryllium 360
Both Monel 400 and nickel beryllium 360 are nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is Monel 400 and the bottom bar is nickel beryllium 360.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 160 | |
200 |
Elongation at Break, % | 20 to 40 | |
1.0 to 30 |
Fatigue Strength, MPa | 230 to 290 | |
260 to 710 |
Poisson's Ratio | 0.32 | |
0.3 |
Shear Modulus, GPa | 62 | |
77 |
Shear Strength, MPa | 370 to 490 | |
510 to 1100 |
Tensile Strength: Ultimate (UTS), MPa | 540 to 780 | |
780 to 1860 |
Tensile Strength: Yield (Proof), MPa | 210 to 590 | |
380 to 1590 |
Thermal Properties
Melting Completion (Liquidus), °C | 1350 | |
1330 |
Melting Onset (Solidus), °C | 1300 | |
1200 |
Specific Heat Capacity, J/kg-K | 430 | |
460 |
Thermal Conductivity, W/m-K | 23 | |
48 |
Thermal Expansion, µm/m-K | 14 | |
14 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 3.3 | |
5.0 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 3.4 | |
5.4 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.9 | |
8.3 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 180 | |
12 to 190 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 1080 | |
360 to 3440 |
Stiffness to Weight: Axial, points | 10 | |
13 |
Stiffness to Weight: Bending, points | 21 | |
24 |
Strength to Weight: Axial, points | 17 to 25 | |
26 to 62 |
Strength to Weight: Bending, points | 17 to 21 | |
23 to 41 |
Thermal Diffusivity, mm2/s | 6.1 | |
13 |
Thermal Shock Resistance, points | 17 to 25 | |
19 to 46 |