Monel 400 vs. C71500 Copper-nickel
Monel 400 belongs to the nickel alloys classification, while C71500 copper-nickel belongs to the copper alloys. They have 63% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is Monel 400 and the bottom bar is C71500 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 160 | |
| 140 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 62 | |
| 52 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 780 | |
| 380 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 1000 | |
| 260 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1240 |
| Melting Onset (Solidus), °C | 1300 | |
| 1170 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 400 |
| Thermal Conductivity, W/m-K | 23 | |
| 28 |
| Thermal Expansion, µm/m-K | 14 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.3 | |
| 4.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.4 | |
| 4.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 50 | |
| 41 |
| Calomel Potential, mV | -80 | |
| -250 |
| Density, g/cm3 | 8.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 5.1 |
| Embodied Energy, MJ/kg | 110 | |
| 74 |
| Embodied Water, L/kg | 250 | |
| 280 |
Common Calculations
| Stiffness to Weight: Axial, points | 10 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 21 | |
| 19 |
| Strength to Weight: Axial, points | 17 to 25 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 17 to 21 | |
| 13 to 18 |
| Thermal Diffusivity, mm2/s | 6.1 | |
| 7.7 |
| Thermal Shock Resistance, points | 17 to 25 | |
| 12 to 20 |
Alloy Composition
| Carbon (C), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 28 to 34 | |
| 63.5 to 70.6 |
| Iron (Fe), % | 0 to 2.5 | |
| 0.4 to 1.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 63 to 72 | |
| 29 to 33 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.024 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.5 |