Monel 400 vs. R60802 Alloy
Monel 400 belongs to the nickel alloys classification, while R60802 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is Monel 400 and the bottom bar is R60802 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 160 | |
| 98 |
| Elongation at Break, % | 20 to 40 | |
| 22 |
| Poisson's Ratio | 0.32 | |
| 0.34 |
| Shear Modulus, GPa | 62 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 780 | |
| 430 |
| Tensile Strength: Yield (Proof), MPa | 210 to 590 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 270 |
| Thermal Conductivity, W/m-K | 23 | |
| 22 |
| Thermal Expansion, µm/m-K | 14 | |
| 6.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 6.5 |
| Embodied Water, L/kg | 250 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 180 | |
| 85 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 1080 | |
| 380 |
| Stiffness to Weight: Axial, points | 10 | |
| 8.3 |
| Stiffness to Weight: Bending, points | 21 | |
| 23 |
| Strength to Weight: Axial, points | 17 to 25 | |
| 18 |
| Strength to Weight: Bending, points | 17 to 21 | |
| 19 |
| Thermal Diffusivity, mm2/s | 6.1 | |
| 12 |
| Thermal Shock Resistance, points | 17 to 25 | |
| 53 |
Alloy Composition
| Carbon (C), % | 0 to 0.3 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.050 to 0.15 |
| Copper (Cu), % | 28 to 34 | |
| 0 |
| Iron (Fe), % | 0 to 2.5 | |
| 0.070 to 0.2 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 |
| Nickel (Ni), % | 63 to 72 | |
| 0.030 to 0.080 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.024 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.2 to 1.7 |
| Zirconium (Zr), % | 0 | |
| 97.8 to 98.7 |
| Residuals, % | 0 | |
| 0 to 0.11 |