Mullite vs. Baria-alkali-silica Glass
Mullite belongs to the oxide-based engineering ceramics classification, while baria-alkali-silica glass belongs to the glass and glass-ceramics. There are 9 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is mullite and the bottom bar is baria-alkali-silica glass.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 2.7 to 3.0 | |
| 3.0 |
| Dielectric Constant (Relative Permittivity) At 1 Hz | 8.0 | |
| 7.0 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 to 170 | |
| 80 |
| Electrical Dissipation At 1 MHz | 0.0025 | |
| 0.0022 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 10 to 11 | |
| 12 |
| Flexural Strength, MPa | 130 to 160 | |
| 34 |
| Stiffness to Weight: Axial, points | 22 to 31 | |
| 15 |
| Stiffness to Weight: Bending, points | 58 to 62 | |
| 48 |
| Thermal Expansion, µm/m-K | 5.8 | |
| 9.5 |