Nickel 693 vs. EN 1.0528 Steel

Nickel 693 belongs to the nickel alloys classification, while EN 1.0528 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is nickel 693 and the bottom bar is EN 1.0528 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
20
Fatigue Strength, MPa 230
180
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 440
320
Tensile Strength: Ultimate (UTS), MPa 660
520
Tensile Strength: Yield (Proof), MPa 310
260

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 1010
400
Melting Completion (Liquidus), °C 1350
1460
Melting Onset (Solidus), °C 1310
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 9.1
48
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 60
2.1
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 9.9
1.4
Embodied Energy, MJ/kg 140
19
Embodied Water, L/kg 320
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
88
Resilience: Unit (Modulus of Resilience), kJ/m3 250
180
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
18
Strength to Weight: Bending, points 21
18
Thermal Diffusivity, mm2/s 2.3
13
Thermal Shock Resistance, points 19
16

Alloy Composition

Aluminum (Al), % 2.5 to 4.0
0
Carbon (C), % 0 to 0.15
0.27 to 0.34
Chromium (Cr), % 27 to 31
0 to 0.4
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 2.5 to 6.0
97.5 to 99.23
Manganese (Mn), % 0 to 1.0
0.5 to 0.8
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 53.3 to 67.5
0 to 0.4
Niobium (Nb), % 0.5 to 2.5
0
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.045
Titanium (Ti), % 0 to 1.0
0