Nickel 693 vs. N10629 Nickel
Both nickel 693 and N10629 nickel are nickel alloys. Both are furnished in the annealed condition. They have 66% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is nickel 693 and the bottom bar is N10629 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 220 |
| Elongation at Break, % | 34 | |
| 45 |
| Fatigue Strength, MPa | 230 | |
| 340 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 76 | |
| 83 |
| Shear Strength, MPa | 440 | |
| 600 |
| Tensile Strength: Ultimate (UTS), MPa | 660 | |
| 860 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 1010 | |
| 910 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1610 |
| Melting Onset (Solidus), °C | 1310 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Expansion, µm/m-K | 13 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 75 |
| Density, g/cm3 | 8.1 | |
| 9.2 |
| Embodied Carbon, kg CO2/kg material | 9.9 | |
| 15 |
| Embodied Energy, MJ/kg | 140 | |
| 190 |
| Embodied Water, L/kg | 320 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 | |
| 320 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 | |
| 360 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 22 |
| Strength to Weight: Axial, points | 23 | |
| 26 |
| Strength to Weight: Bending, points | 21 | |
| 22 |
| Thermal Shock Resistance, points | 19 | |
| 27 |
Alloy Composition
| Aluminum (Al), % | 2.5 to 4.0 | |
| 0.1 to 0.5 |
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.010 |
| Chromium (Cr), % | 27 to 31 | |
| 0.5 to 1.5 |
| Cobalt (Co), % | 0 | |
| 0 to 2.5 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.5 |
| Iron (Fe), % | 2.5 to 6.0 | |
| 1.0 to 6.0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 26 to 30 |
| Nickel (Ni), % | 53.3 to 67.5 | |
| 65 to 72.4 |
| Niobium (Nb), % | 0.5 to 2.5 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.050 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 to 1.0 | |
| 0 |