Nickel Beryllium 360 vs. Grade 23 Titanium
Nickel beryllium 360 belongs to the nickel alloys classification, while grade 23 titanium belongs to the titanium alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is nickel beryllium 360 and the bottom bar is grade 23 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Elongation at Break, % | 1.0 to 30 | |
| 6.7 to 11 |
| Fatigue Strength, MPa | 260 to 710 | |
| 470 to 500 |
| Poisson's Ratio | 0.3 | |
| 0.32 |
| Shear Modulus, GPa | 77 | |
| 40 |
| Shear Strength, MPa | 510 to 1100 | |
| 540 to 570 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 1860 | |
| 930 to 940 |
| Tensile Strength: Yield (Proof), MPa | 380 to 1590 | |
| 850 to 870 |
Thermal Properties
| Melting Completion (Liquidus), °C | 1330 | |
| 1610 |
| Melting Onset (Solidus), °C | 1200 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 560 |
| Thermal Conductivity, W/m-K | 48 | |
| 7.1 |
| Thermal Expansion, µm/m-K | 14 | |
| 9.4 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.0 | |
| 1.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.4 | |
| 2.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 4.4 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 190 | |
| 61 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 to 3440 | |
| 3430 to 3560 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 35 |
| Strength to Weight: Axial, points | 26 to 62 | |
| 58 to 59 |
| Strength to Weight: Bending, points | 23 to 41 | |
| 48 |
| Thermal Diffusivity, mm2/s | 13 | |
| 2.9 |
| Thermal Shock Resistance, points | 19 to 46 | |
| 67 to 68 |